<data xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance">
<row _id="1"><ID>1</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>27.04.2022</Test Date><Test Piece Identifier>A</Test Piece Identifier><Test Piece Composition>CuZn38As</Test Piece Composition><Test Piece Provider>DKI</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>8 x 8 x 8</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>1346</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213.3</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>2</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>207.45</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>215.5</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>0.141421356237301</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.84</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>21</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>A1</Indentation ID1><indentation_horizontal_diagonal1___m_>270.47</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>279.52</indentation_vertical_diagonal1___m_><Indentation ID2>A2</Indentation ID2><indentation_horizontal_diagonal2___m_>271.77</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>277.2</indentation_vertical_diagonal2___m_><Indentation ID3>A3</Indentation ID3><indentation_horizontal_diagonal3___m_>269.96</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>276.42</indentation_vertical_diagonal3___m_><Indentation ID4>A4</Indentation ID4><indentation_horizontal_diagonal4___m_>267.89</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>273.32</indentation_vertical_diagonal4___m_><Indentation ID5>A5</Indentation ID5><indentation_horizontal_diagonal5___m_>267.37109375</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>277.2</indentation_vertical_diagonal5___m_><Indentation ID6>A6</Indentation ID6><indentation_horizontal_diagonal6___m_ xsi:nil="true" /><indentation_vertical_diagonal6___m_ xsi:nil="true" /><indentation_average_diagonal1___m_>274.995</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>274.485</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>273.19</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>270.605</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>272.285546875</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_ xsi:nil="true" /><total_average_diagonal___m_>273.112109375</total_average_diagonal___m_><vickers_hardness1__hv_5_>122.6</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>123.1</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>124.3</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>126.6</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>125.1</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_ xsi:nil="true" /><vickers_hardness_average__hv_5_>124.34</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>1.6009372255026115</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>0.26021529547663386</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.06834120422262913</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.417123933401698</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>4.866021434318795</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>1.031411157993431</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>5.897432592312226</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>124 ± 6</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="2"><ID>2</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>27.04.2022</Test Date><Test Piece Identifier>B</Test Piece Identifier><Test Piece Composition>CuZn21Si3P</Test Piece Composition><Test Piece Provider>DKI</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>8 x 8 x 8</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>1346</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213.3</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>2</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>207.45</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>215.5</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>0.141421356237301</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.84</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>21</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>B1</Indentation ID1><indentation_horizontal_diagonal1___m_>204.28</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>201.69</indentation_vertical_diagonal1___m_><Indentation ID2>B2</Indentation ID2><indentation_horizontal_diagonal2___m_>205.83</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>204.28</indentation_vertical_diagonal2___m_><Indentation ID3>B3</Indentation ID3><indentation_horizontal_diagonal3___m_>206.86</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>202.73</indentation_vertical_diagonal3___m_><Indentation ID4>B4</Indentation ID4><indentation_horizontal_diagonal4___m_>208.93</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>201.17</indentation_vertical_diagonal4___m_><Indentation ID5>B5</Indentation ID5><indentation_horizontal_diagonal5___m_>209.45</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>201.17</indentation_vertical_diagonal5___m_><Indentation ID6>B6</Indentation ID6><indentation_horizontal_diagonal6___m_ xsi:nil="true" /><indentation_vertical_diagonal6___m_ xsi:nil="true" /><indentation_average_diagonal1___m_>202.985</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>205.055</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>204.79500000000002</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>205.05</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>205.31</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_ xsi:nil="true" /><total_average_diagonal___m_>204.63899999999998</total_average_diagonal___m_><vickers_hardness1__hv_5_>225.1</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>220.5</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>221.1</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>220.6</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>220</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_ xsi:nil="true" /><vickers_hardness_average__hv_5_>221.46000000000004</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>2.0719555979798394</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>0.26021529547663386</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.16244996095480813</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.417123933401698</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>4.883842785779135</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>1.031411157993431</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>5.915253943772566</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>221± 6</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="3"><ID>3</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>27.04.2022</Test Date><Test Piece Identifier>C</Test Piece Identifier><Test Piece Composition>CuNiSi</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>8 x 8 x 8</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>1346</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213.3</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>2</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>207.45</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>215.5</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>0.141421356237301</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.84</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>21</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>C1</Indentation ID1><indentation_horizontal_diagonal1___m_>348.31</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>346.75</indentation_vertical_diagonal1___m_><Indentation ID2>C2</Indentation ID2><indentation_horizontal_diagonal2___m_>358.65</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>367.44</indentation_vertical_diagonal2___m_><Indentation ID3>C3</Indentation ID3><indentation_horizontal_diagonal3___m_>351.41</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>364.86</indentation_vertical_diagonal3___m_><Indentation ID4>C4</Indentation ID4><indentation_horizontal_diagonal4___m_>348.31</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>364.08</indentation_vertical_diagonal4___m_><Indentation ID5>C5</Indentation ID5><indentation_horizontal_diagonal5___m_>359.17</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>364.08</indentation_vertical_diagonal5___m_><Indentation ID6>C6</Indentation ID6><indentation_horizontal_diagonal6___m_ xsi:nil="true" /><indentation_vertical_diagonal6___m_ xsi:nil="true" /><indentation_average_diagonal1___m_>347.53</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>363.04499999999996</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>358.135</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>356.195</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>361.625</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_ xsi:nil="true" /><total_average_diagonal___m_>357.306</total_average_diagonal___m_><vickers_hardness1__hv_5_>76.8</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>70.4</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>72.3</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>73.1</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>70.9</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_ xsi:nil="true" /><vickers_hardness_average__hv_5_>72.7</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>2.532785028382784</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>0.26021529547663386</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.030542657521066836</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.417123933401698</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>4.862948001893578</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>1.031411157993431</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>5.894359159887009</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>73 ± 6</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="4"><ID>4</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>27.04.2022</Test Date><Test Piece Identifier>D</Test Piece Identifier><Test Piece Composition>CuSn6</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>8 x 8 x 8</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>1346</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213.3</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>2</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>207.45</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>215.5</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>0.141421356237301</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.84</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>21</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>D1</Indentation ID1><indentation_horizontal_diagonal1___m_>295.3</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>300.21</indentation_vertical_diagonal1___m_><Indentation ID2>D2</Indentation ID2><indentation_horizontal_diagonal2___m_>304.35</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>303.57</indentation_vertical_diagonal2___m_><Indentation ID3>D3</Indentation ID3><indentation_horizontal_diagonal3___m_>325.55</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>328.14</indentation_vertical_diagonal3___m_><Indentation ID4>D4</Indentation ID4><indentation_horizontal_diagonal4___m_>293.49</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>297.11</indentation_vertical_diagonal4___m_><Indentation ID5>D5</Indentation ID5><indentation_horizontal_diagonal5___m_>297.37</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>300.99</indentation_vertical_diagonal5___m_><Indentation ID6>D6</Indentation ID6><indentation_horizontal_diagonal6___m_ xsi:nil="true" /><indentation_vertical_diagonal6___m_ xsi:nil="true" /><indentation_average_diagonal1___m_>297.755</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>303.96000000000004</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>326.845</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>295.3</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>299.18</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_ xsi:nil="true" /><total_average_diagonal___m_>304.60800000000006</total_average_diagonal___m_><vickers_hardness1__hv_5_>104.6</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>100.4</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>86.8</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>106.3</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>103.6</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_ xsi:nil="true" /><vickers_hardness_average__hv_5_>100.34</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>7.868163699364674</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>0.26021529547663386</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.04944763355764337</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.417123933401698</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>4.8641917093602265</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>1.031411157993431</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>5.895602867353658</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>100 ± 6</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="5"><ID>5</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>27.04.2022</Test Date><Test Piece Identifier>E</Test Piece Identifier><Test Piece Composition>CuSn12</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>8 x 8 x 8</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>1346</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213.3</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>2</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>207.45</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>215.5</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>0.141421356237301</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.84</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>21</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>E1</Indentation ID1><indentation_horizontal_diagonal1___m_>238.93</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>240.48</indentation_vertical_diagonal1___m_><Indentation ID2>E2</Indentation ID2><indentation_horizontal_diagonal2___m_>241</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>247.98</indentation_vertical_diagonal2___m_><Indentation ID3>E3</Indentation ID3><indentation_horizontal_diagonal3___m_>239.7</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>248.24</indentation_vertical_diagonal3___m_><Indentation ID4>E4</Indentation ID4><indentation_horizontal_diagonal4___m_>239.7</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>241.77</indentation_vertical_diagonal4___m_><Indentation ID5>E5</Indentation ID5><indentation_horizontal_diagonal5___m_>234.79</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>237.38</indentation_vertical_diagonal5___m_><Indentation ID6>E6</Indentation ID6><indentation_horizontal_diagonal6___m_ xsi:nil="true" /><indentation_vertical_diagonal6___m_ xsi:nil="true" /><indentation_average_diagonal1___m_>239.70499999999998</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>244.49</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>243.97</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>240.735</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>236.08499999999998</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_ xsi:nil="true" /><total_average_diagonal___m_>240.99699999999999</total_average_diagonal___m_><vickers_hardness1__hv_5_>161.4</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>155.1</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>155.8</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>160</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>166.4</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_ xsi:nil="true" /><vickers_hardness_average__hv_5_>159.73999999999998</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>4.588899650242966</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>0.26021529547663386</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.0994980946654573</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.417123933401698</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>4.870318203611506</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>1.031411157993431</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>5.901729361604937</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>160 ± 6</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="6"><ID>6</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>27.04.2022</Test Date><Test Piece Identifier>F</Test Piece Identifier><Test Piece Composition>CuNi12Al3</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>8 x 8 x 8</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>1346</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213.3</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>2</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>207.45</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>215.5</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>0.141421356237301</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.84</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>21</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>F1</Indentation ID1><indentation_horizontal_diagonal1___m_>181.78</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>179.97</indentation_vertical_diagonal1___m_><Indentation ID2>F2</Indentation ID2><indentation_horizontal_diagonal2___m_>185.66</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>181.01</indentation_vertical_diagonal2___m_><Indentation ID3>F3</Indentation ID3><indentation_horizontal_diagonal3___m_>189.54</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>183.33</indentation_vertical_diagonal3___m_><Indentation ID4>F4</Indentation ID4><indentation_horizontal_diagonal4___m_>190.57</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>188.5</indentation_vertical_diagonal4___m_><Indentation ID5>F5</Indentation ID5><indentation_horizontal_diagonal5___m_>177.64</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>183.85</indentation_vertical_diagonal5___m_><Indentation ID6>F6</Indentation ID6><indentation_horizontal_diagonal6___m_ xsi:nil="true" /><indentation_vertical_diagonal6___m_ xsi:nil="true" /><indentation_average_diagonal1___m_>180.875</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>183.33499999999998</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>186.435</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>189.535</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>180.745</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_ xsi:nil="true" /><total_average_diagonal___m_>184.185</total_average_diagonal___m_><vickers_hardness1__hv_5_>283.5</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>275.9</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>266.8</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>258.1</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>283.9</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_ xsi:nil="true" /><vickers_hardness_average__hv_5_>273.64000000000004</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>11.13409179053234</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>0.26021529547663386</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.22301703825975397</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.417123933401698</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>4.902927006648821</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>1.031411157993431</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>5.934338164642252</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>274 ± 6</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="7"><ID>7</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>09.01.2023</Test Date><Test Piece Identifier>G10</Test Piece Identifier><Test Piece Composition>CuNi6Sn4</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>3.14x9x9x15</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>3424</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>5</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>208.05</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>214.2</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>1.471</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.14</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>22</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>G10-1</Indentation ID1><indentation_horizontal_diagonal1___m_>280.92</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>277.86</indentation_vertical_diagonal1___m_><Indentation ID2>G10-2</Indentation ID2><indentation_horizontal_diagonal2___m_>282.4</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>282.71</indentation_vertical_diagonal2___m_><Indentation ID3>G10-3</Indentation ID3><indentation_horizontal_diagonal3___m_>267.52</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>270.94</indentation_vertical_diagonal3___m_><Indentation ID4>G10-4</Indentation ID4><indentation_horizontal_diagonal4___m_>299.02</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>295.19</indentation_vertical_diagonal4___m_><Indentation ID5>G10-5</Indentation ID5><indentation_horizontal_diagonal5___m_>289.2</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>289.62</indentation_vertical_diagonal5___m_><Indentation ID6>G10-6</Indentation ID6><indentation_horizontal_diagonal6___m_>289.71</indentation_horizontal_diagonal6___m_><indentation_vertical_diagonal6___m_>286.9</indentation_vertical_diagonal6___m_><indentation_average_diagonal1___m_>279.39</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>282.56</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>269.23</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>297.11</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>289.41</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_>288.31</indentation_average_diagonal6___m_><total_average_diagonal___m_>284.34</total_average_diagonal___m_><vickers_hardness1__hv_5_>118.8</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>116.2</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>127.9</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>105.1</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>110.7</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_>111.6</vickers_hardness6__hv_5_><vickers_hardness_average__hv_5_>115.1</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>7.88</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>1.6769399999999999</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.06076452189550798</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.5239247133023595</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>6.0629063579312445</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>0.5633802816901355</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>6.62628663962138</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>115 ± 7</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="8"><ID>8</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>09.01.2023</Test Date><Test Piece Identifier>G22</Test Piece Identifier><Test Piece Composition>CuNi6Sn4</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>3.14x9x9x15</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>3424</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>5</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>208.05</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>214.2</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>1.471</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.14</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>22</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>G22-1</Indentation ID1><indentation_horizontal_diagonal1___m_>254.56</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>254.07</indentation_vertical_diagonal1___m_><Indentation ID2>G22-2</Indentation ID2><indentation_horizontal_diagonal2___m_>256.39</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>260.04</indentation_vertical_diagonal2___m_><Indentation ID3>G22-3</Indentation ID3><indentation_horizontal_diagonal3___m_>257.17</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>261.1</indentation_vertical_diagonal3___m_><Indentation ID4>G22-4</Indentation ID4><indentation_horizontal_diagonal4___m_>255.4</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>263.16</indentation_vertical_diagonal4___m_><Indentation ID5>G22-5</Indentation ID5><indentation_horizontal_diagonal5___m_>276.03</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>275.78</indentation_vertical_diagonal5___m_><Indentation ID6>G22-6</Indentation ID6><indentation_horizontal_diagonal6___m_>253.23</indentation_horizontal_diagonal6___m_><indentation_vertical_diagonal6___m_>256.09</indentation_vertical_diagonal6___m_><indentation_average_diagonal1___m_>254.32</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>258.22</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>259.14</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>259.28</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>275.91</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_>254.66</indentation_average_diagonal6___m_><total_average_diagonal___m_>260.26</total_average_diagonal___m_><vickers_hardness1__hv_5_>143.4</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>139.1</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>138.1</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>137.9</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>121.8</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_>143</vickers_hardness6__hv_5_><vickers_hardness_average__hv_5_>137.2</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>7.927</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>1.6769399999999999</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.07913332360920743</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.5239247133023595</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>6.06460151628424</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>0.5633802816901355</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>6.627981797974376</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>137 ± 7</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="9"><ID>9</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>09.01.2023</Test Date><Test Piece Identifier>H10</Test Piece Identifier><Test Piece Composition>CuSn8Ni2</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>3.14x9x9x15</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>3424</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>5</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>208.05</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>214.2</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>1.471</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.14</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>22</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>H10-1</Indentation ID1><indentation_horizontal_diagonal1___m_>289.75</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>295.02</indentation_vertical_diagonal1___m_><Indentation ID2>H10-2</Indentation ID2><indentation_horizontal_diagonal2___m_>287.17</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>279.58</indentation_vertical_diagonal2___m_><Indentation ID3>H10-3</Indentation ID3><indentation_horizontal_diagonal3___m_>288.94</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>301.41</indentation_vertical_diagonal3___m_><Indentation ID4>H10-4</Indentation ID4><indentation_horizontal_diagonal4___m_>283.8896484375</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>297.04</indentation_vertical_diagonal4___m_><Indentation ID5>H10-5</Indentation ID5><indentation_horizontal_diagonal5___m_>283.24</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>295.63</indentation_vertical_diagonal5___m_><Indentation ID6>H10-6</Indentation ID6><indentation_horizontal_diagonal6___m_>287.7</indentation_horizontal_diagonal6___m_><indentation_vertical_diagonal6___m_>291.09</indentation_vertical_diagonal6___m_><indentation_average_diagonal1___m_>292.39</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>283.38</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>295.18</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>290.46</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>289.44</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_>289.4</indentation_average_diagonal6___m_><total_average_diagonal___m_>290.04</total_average_diagonal___m_><vickers_hardness1__hv_5_>108.5</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>115.5</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>106.4</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>109.9</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>110.7</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_>110.7</vickers_hardness6__hv_5_><vickers_hardness_average__hv_5_>110.3</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>3.032</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>1.6769399999999999</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.057086095089712054</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.5239247133023595</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>6.062620346524621</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>0.5633802816901355</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>6.626000628214757</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>110 ± 7</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="10"><ID>10</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>09.01.2023</Test Date><Test Piece Identifier>H22</Test Piece Identifier><Test Piece Composition>CuSn8Ni2</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>3.14x9x9x15</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>3424</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>5</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>208.05</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>214.2</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>1.471</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.14</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>22</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>H22-1</Indentation ID1><indentation_horizontal_diagonal1___m_>295.41</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>292.89</indentation_vertical_diagonal1___m_><Indentation ID2>H22-2</Indentation ID2><indentation_horizontal_diagonal2___m_>296.2</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>295.15</indentation_vertical_diagonal2___m_><Indentation ID3>H22-3</Indentation ID3><indentation_horizontal_diagonal3___m_>301.49</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>295.77</indentation_vertical_diagonal3___m_><Indentation ID4>H22-4</Indentation ID4><indentation_horizontal_diagonal4___m_>293.32</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>282.78</indentation_vertical_diagonal4___m_><Indentation ID5>H22-5</Indentation ID5><indentation_horizontal_diagonal5___m_>291.32</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>284.87</indentation_vertical_diagonal5___m_><Indentation ID6>H22-6</Indentation ID6><indentation_horizontal_diagonal6___m_>292.58</indentation_horizontal_diagonal6___m_><indentation_vertical_diagonal6___m_>283.95</indentation_vertical_diagonal6___m_><indentation_average_diagonal1___m_>294.15</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>295.68</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>298.63</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>288.05</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>288.1</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_>288.27</indentation_average_diagonal6___m_><total_average_diagonal___m_>292.15</total_average_diagonal___m_><vickers_hardness1__hv_5_>107.2</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>106.1</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>104</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>111.8</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>111.7</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_>111.6</vickers_hardness6__hv_5_><vickers_hardness_average__hv_5_>108.7</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>3.409</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>1.6769399999999999</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.05585169710024714</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.5239247133023595</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>6.062528365675942</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>0.5633802816901355</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>6.625908647366078</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>109 ± 7</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="11"><ID>11</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>09.01.2023</Test Date><Test Piece Identifier>I9</Test Piece Identifier><Test Piece Composition>CuZn23Si2.5</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>3.14x9x9x15</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>3424</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>5</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>208.05</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>214.2</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>1.471</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.14</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>22</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>I9-1</Indentation ID1><indentation_horizontal_diagonal1___m_>287.92</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>284.38</indentation_vertical_diagonal1___m_><Indentation ID2>I9-2</Indentation ID2><indentation_horizontal_diagonal2___m_>283.77</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>282.75</indentation_vertical_diagonal2___m_><Indentation ID3>I9-3</Indentation ID3><indentation_horizontal_diagonal3___m_>282.22</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>285.05</indentation_vertical_diagonal3___m_><Indentation ID4>I9-4</Indentation ID4><indentation_horizontal_diagonal4___m_>283.81</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>281.26</indentation_vertical_diagonal4___m_><Indentation ID5>I9-5</Indentation ID5><indentation_horizontal_diagonal5___m_>284.32</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>281.17578125</indentation_vertical_diagonal5___m_><Indentation ID6>I9-6</Indentation ID6><indentation_horizontal_diagonal6___m_>283.29</indentation_horizontal_diagonal6___m_><indentation_vertical_diagonal6___m_>281.43</indentation_vertical_diagonal6___m_><indentation_average_diagonal1___m_>286.15</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>283.26</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>283.64</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>282.54</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>282.75</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_>282.36</indentation_average_diagonal6___m_><total_average_diagonal___m_>283.45</total_average_diagonal___m_><vickers_hardness1__hv_5_>113.3</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>115.6</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>115.3</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>116.2</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>116</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_>116.3</vickers_hardness6__hv_5_><vickers_hardness_average__hv_5_>115.5</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>1.118</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>1.6769399999999999</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.06116714970458444</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.5239247133023595</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>6.062938746985447</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>0.5633802816901355</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>6.626319028675582</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>116 ± 7</final_vickers_hardness_and_uncetainity__hv_5_></row>
<row _id="12"><ID>12</ID><Test Standard>DIN EN ISO 6507-1:2018</Test Standard><Test Date>09.01.2023</Test Date><Test Piece Identifier>I20</Test Piece Identifier><Test Piece Composition>CuZn23Si2.5</Test Piece Composition><Test Piece Provider>fem</Test Piece Provider><Test Piece Preparation>Smoothing, polishing, and cleaning steps according to the standard</Test Piece Preparation><test_piece_dimension__mxmxm_>3.14x9x9x15</test_piece_dimension__mxmxm_><testing_machine_diagonal_measuring_system>KB 30 SR FA Basic</testing_machine_diagonal_measuring_system><Indenter Identifier>3424</Indenter Identifier><Indenter Material Identifier>Diamond</Indenter Material Identifier><indenter_angle____>136</indenter_angle____><Measuring system resolution>in the standard range</Measuring system resolution><CRM Identifier>8890101.062</CRM Identifier><crm_certified_vickers_hardness__hv_5_>213</crm_certified_vickers_hardness__hv_5_><CRM Vickers Hardness-Indentation number>5</CRM Vickers Hardness-Indentation number><crm_vickers_hardness_average_diagonal___m_>208.05</crm_vickers_hardness_average_diagonal___m_><crm_average_vickers_hardness__hv_5_>214.2</crm_average_vickers_hardness__hv_5_><crm_standard_deviation_vickers_hardness__hv_5_>1.471</crm_standard_deviation_vickers_hardness__hv_5_><crm_uncertainty__ucrm___hv_5_>2.4</crm_uncertainty__ucrm___hv_5_><CRM t constant>1.14</CRM t constant><CRM Sigma ms Constant>0.00026</CRM Sigma ms Constant><test_temperature___c_>22</test_temperature___c_><test_force__n_>49.03</test_force__n_><test_point_edge_distance__mm_>in the standard range</test_point_edge_distance__mm_><test_points_distance__mm_>in the standard range</test_points_distance__mm_><loading_time__s_>14</loading_time__s_><Indentation ID1>I20-1</Indentation ID1><indentation_horizontal_diagonal1___m_>291.03</indentation_horizontal_diagonal1___m_><indentation_vertical_diagonal1___m_>300.19</indentation_vertical_diagonal1___m_><Indentation ID2>I20-2</Indentation ID2><indentation_horizontal_diagonal2___m_>292.63</indentation_horizontal_diagonal2___m_><indentation_vertical_diagonal2___m_>294.82</indentation_vertical_diagonal2___m_><Indentation ID3>I20-3</Indentation ID3><indentation_horizontal_diagonal3___m_>290.04</indentation_horizontal_diagonal3___m_><indentation_vertical_diagonal3___m_>286.63</indentation_vertical_diagonal3___m_><Indentation ID4>I20-4</Indentation ID4><indentation_horizontal_diagonal4___m_>285.9</indentation_horizontal_diagonal4___m_><indentation_vertical_diagonal4___m_>289.84</indentation_vertical_diagonal4___m_><Indentation ID5>I20-5</Indentation ID5><indentation_horizontal_diagonal5___m_>287.72</indentation_horizontal_diagonal5___m_><indentation_vertical_diagonal5___m_>292.14</indentation_vertical_diagonal5___m_><Indentation ID6>I20-6</Indentation ID6><indentation_horizontal_diagonal6___m_>290.81</indentation_horizontal_diagonal6___m_><indentation_vertical_diagonal6___m_>293.13</indentation_vertical_diagonal6___m_><indentation_average_diagonal1___m_>295.61</indentation_average_diagonal1___m_><indentation_average_diagonal2___m_>293.73</indentation_average_diagonal2___m_><indentation_average_diagonal3___m_>288.34</indentation_average_diagonal3___m_><indentation_average_diagonal4___m_>287.87</indentation_average_diagonal4___m_><indentation_average_diagonal5___m_>289.93</indentation_average_diagonal5___m_><indentation_average_diagonal6___m_>291.97</indentation_average_diagonal6___m_><total_average_diagonal___m_>291.24</total_average_diagonal___m_><vickers_hardness1__hv_5_>106.1</vickers_hardness1__hv_5_><vickers_hardness2__hv_5_>107.5</vickers_hardness2__hv_5_><vickers_hardness3__hv_5_>111.5</vickers_hardness3__hv_5_><vickers_hardness4__hv_5_>111.9</vickers_hardness4__hv_5_><vickers_hardness5__hv_5_>110.3</vickers_hardness5__hv_5_><vickers_hardness6__hv_5_>108.8</vickers_hardness6__hv_5_><vickers_hardness_average__hv_5_>109.4</vickers_hardness_average__hv_5_><vickers_hardness_standard_deviation__hv_5_>2.294</vickers_hardness_standard_deviation__hv_5_><testing_machine_uncertainty__uh___hv_5_>1.6769399999999999</testing_machine_uncertainty__uh___hv_5_><measurement_resolution_uncertainty__ums___hv_5_>-0.056387004040755785</measurement_resolution_uncertainty__ums___hv_5_><bias_uncertainty__uhtm___hv_5_>2.5239247133023595</bias_uncertainty__uhtm___hv_5_><vickers_uncertainty_um1__hv_5_>6.0625680071955586</vickers_uncertainty_um1__hv_5_><vickers_hardness_bias__hv_5_>0.5633802816901355</vickers_hardness_bias__hv_5_><vickers_hardness_uncetainity__hv_5_>6.625948288885694</vickers_hardness_uncetainity__hv_5_><final_vickers_hardness_and_uncetainity__hv_5_>109 ± 7</final_vickers_hardness_and_uncetainity__hv_5_></row>
</data>